Mask Making Silicone Rubber

1. Description

RT-8 series silicone is great to make silicone mask products in Hollywood favorites and film industry. Which is a medical silicone for mask making or skin. It’s non-toxic, without any side effects to human body, you can ware it safely. And breath freely by your nostrils and you can open or close your mouth anytime.


* very soft

*very strong

* very “stretchy”

*Low viscosity

* Odorless

* Long casting

*Skin safe & medical grade

*Easy processing - mixing ratio 1 : 1

*Adjustable working time and curing time


1. Mixing the two components The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase. It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.

2. Degassing The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure. Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.

3. Polymerisation The system polymerises at 23°C. The curing may be slowed down at lower temperature and contrary accelerated by heat. Contact with certain materials can inhibit the crosslinking. See list below:

• natural rubbers vulcanised with sulphur

• RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds

• PVC stabilised with tin salts and additives

• epoxy resins catalysed with amines

In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area

4. Package

Part A:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.

Part B:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.

5. Storage and shelf life

When stored in their original unopened packaging, at a temperature of between -10°C and +30°C, the RTV GC-808 A & B can be stored for 12 months from the date of manufacture clearly marked on the packaging. Beyond this date, GC Silicone no longer guarantees that the products meet the sales specifications.

6.Technical Data

Characteristics of the non cured product

Appearancelow viscous liquid
Density [g/cm 3 ] at 23 °C, approx1.081.081.08
Viscosity [mPa·s] at 23 °C, approx3000±10004000±10004000±1000


Curing conditions: 1h at 80 °C

Hardness Shore A5±210±215±2
Tensile strength [ ]30±535±535±5
Elongation [%]≥550≥550≥550
Tear strength [kg/cm]8±212±214±2


  • Follow Us
  • Whatsapp: 86-18038384659
  • Skype: elainemin11
  • E-mail:
  • Tel: 86-18038384659
  • Fax: +86 0769 8702 9161
  • Add: No.4 Shichang Street, The 2ND Industrial District Of Xiaobian, Changan, Dongguan, China

Copyright © GUOCHUANG SILICONE CO., LTD. All Rights Reserved   

Online Services